PLA resin, also called Poly lactic acid resin, which is a 100% bio-based degradable eco-friendly resin. This PLA resin is polymerized from lactic acid derived from plant sources such as corn.
Under the background of global ban on plastics, environmental protection, and searching of bio-friendly resins, Poly lactic acid is currently the most competitive material.
Physical Property
|
Poly lactic acid resin |
P180 |
P180S |
P360 |
P380 |
P380S |
M580 |
Test Standard |
|
Density (g/cm3) |
1.24 |
1.28 |
1.24 |
1.35±0.05 |
1.35±0.05 |
1.26 |
GB/T 1033-2008 |
|
Melting Index (g/10min) 190℃, 2.16kg |
3-6 |
3-5 |
15±5 |
15±5 |
15±5 |
3-5 |
GB/T 3682-2000 |
|
Melting Point(℃) |
178±3 |
\ |
165±3 |
178±3 |
178±3 |
\ |
GB/T 19466.3-2004 |
|
GT Temperature(℃) |
61±2 |
\ |
61±2 |
\ |
61±2 |
\ |
GB/T 19466.2-2004 |
Mechanical Property
|
Poly lactic acid resin |
P180 |
P180S |
P360 |
P380 |
P380S |
M580 |
Test Standard |
|
Tensile strength(MPa)
|
≥55 |
≥25 |
≥50 |
≥45 |
≥45 |
≥25 |
GB/T 1040-2006 |
|
Impact strength(KJ/m2) Izod |
≥3 |
\ |
≥3 |
≥3 |
≥8 |
\ |
GB/T 1043-2008 |
|
Elongation at Break(%) |
≥3 |
≥80 |
≥5 |
≥5 |
≥20 |
≥100 |
GB/T 1040-2006 |
|
Heat Resistant(℃) HDT (amorphous) HDT(crystallize) |
55-60
100-110
|
55-60 |
\ |
55-60
100-110
|
55-60
100-110
|
55-60 |
\ |
APPLICATION 
P180
P180S
P360
P380
P380S
M580
Suggested
Application
Extrusion
(3D printing/ spinning)
Extrusion
(Straw)
Transparent injection
(Cold drinking cup)
Heat resistant injection
(Disposable items)
Heat resistant injection
(Durable goods)
Extrusion
(Blowing film)
WHY CHOOSE US
Professional technical team: senior PLA resin experts leading Asia in bio-based material technology.
Professional R&D team: specialized in the accurate development of bio-based material and products.
Professional after-sales team: able to solve any problems in the use of bio-based materials for over 10 years.
MATERIAL FEATURE
This is suit for various processing method. The heat resistance of products will increase to over 100℃after annealing.
More environmentally: 100% degradable and compostable in industrial compost processing.
More use: different series for extrusion, injection molding, spinning fiber, film or 3D printing.
MARKET ADVANTAGE
PLA lactic acid resin is a degradable material which is eligible to the development direction of global market and policy.
High acceptance: a acknowledged environmental-friendly material conform to different countries or regions.
High security: free from plasticizer, BPA of heavy metals.
High growth: hot in global market with a over 100% annual increase.