Transparent Automobile Paint Car Repair Coating Auto Body Filler Polyester Putty

Sales

Product features: Car Repair Coating Auto Body Filler Polyester Putty

Applicable：Putty, commonly known as putty, also known as unsaturated polyester resin putty, English name: Poly-Putty Base, is a new type of inlay material with rapid development, which can be well attached to the surface of the object and does not produce in the drying process. crack.

Product Detail

Product name	Putty
Substrate	2K Primer or The Surface of Cold-Rolled Plate
Formation Mechanism	Conversion Type
Other Name	Unsaturated Polyester Resin Putty/Car Body Filler
Sanding Property	Easy Grinding
Specification	3L
Components	Unsaturated Polyester Resin

Product Description

Car Repair Coating Auto Body Filler Polyester Putty

The advantages of new solid putty over ordinary putty

1,Paste state: It does not reflect the consistency problem of the putty.

2, Construstiong: Fine texture, smooth coating and scraping properties.

3, Small sand holes: at least 60% less sand holes than ordinary putty.

4, Sanding property: The new solid putty is easily on grinding.

5, High-temperature resistance: High temperature resistance up to 130 degrees.

6, Packability: Grey fine solid, with better packability.

7, Interface: Firm, neat, better interface effect.

8, Flexibility:Higher than the national standard of ordinary putty.

9, Air dying property and adhesion: More suitable for dry grinding and fast repair, more effectively avoid bubbles, cracking and other problems.

10, Economic and efficient: It can save time and greatly improved construction efficiency, because of it's good coating and scraping properties, good air-drying property and good Formability.

Comparative advantages of technical parameters:

	Pot life of scraping	Surface drying time	Sanding time	Flexibility	Adhesion	Impact resistance	Anti-temperature property
New Solid Putty	2.5 min/25ºC	10min/25ºC	50min/25ºC	50mm	2.5Mpa	15	-40ºC--120ºC
Ordinary Putty	5 min/25ºC	20min/25ºC	60min/25ºC	50mm	1.5Mpa	12	Room temperature

Construction range:

Can be used on auto repair iron plate, steel plate, furniture wood, etc.

Main Technical indicators:

Item	Index	Test Method
Flexibility (mm)	≤100	GB/T1748
Impact resistance(kg·cm)	≥13	GB/T1732
Heat resistance of steel plate(Bake at 120 ºC for 1 hour)	no bubble, no bubble	GB/T1735
	no bubble, no bubble	GB/T1735
Adhesion(MPa)	≥2.5	HB/T4561
Water grinding time 25ºC(min)	20	GB/T1728
Grinability	Starch and pulp are obvious	HB/T4561

Application

1, Remove rust, oil, dirt, old film, water,etc. from surface completely by sander and solvent before we use solid putty.

2, The putty and hardener should be mixed evenly in strict accordance with the specified proportion(100:1.5~3), and the color must be consistent, and scraping should be completed within about 3-5 minutes, otherwise it will be scrapped if it become gel.

3, Apply and scrape the adjusted putty on the 2k primer or the surface of cold-rolled plate after grinding. If thick layer is needed, it is better to scrape several times to the required thickness.

4, After thorough hardening, water or dry grinding can be done. 20 to 30 minutes after scraping is the best wet grinding time, and the the best dry grinding time is 1 hour to 1.5 hours(at 25ºC, humidity less than 40%). Make sure the putty is completely dry before spray paints.

Notes:

1, When scraping, if there is bubble infiltration, must be thoroughly scraped with a scraper to ensure good adhesion.

2, The putty which mixed with hardener should not be put back

into the original pot. It should be capped immediately after use for avoiding the deterioration of the putty if solvent

volatilization. It is strictly prohibited to infiltrate into the thinner and other solvents to dilute the solid putty for construction.

3, When the temperature is low and the humidity is high, the curing time of the application will be slightly extended. The consistency of putty and the gel time can be adjusted according to the customer's requirements.

4, This product is compatible with a variety of primers, but it cannot be scraped on phenolic primers or alkyd primers to avoid falling off and bubbling. Make sure the primers are completely dry when applying and scraping putty to avoid falling off together.

5,Matched with special hardener, can not be mixed with other hardener.

6, This product is not suitable for direct coating and scraping on galvanized sheet, aluminum, stainless steel and other plates.

7, It can be stored in a cool place(below 25ºC) for 12 months.

Tags : Car Repair Coating Auto Body Filler Polyester Putty Car Paint Flexible and Easy Sanding Polyester Putty Auto Putty Factory Direct Sales Directly Extra Quick Dry Car Putty Good Quality Nc Putty Auto Paint Car Body Filler f

Leave A Message

If you are interested in our products and want to know more details,please leave a message here,we will reply you as soon as we can.

Subject : Transparent Automobile Paint Car Repair Coating Auto Body Filler Polyester Putty

SUPPLIER

Guangzhou Meklon Chemical Technology Co., Ltd.

Gold Supplier

Visit Store

Sales

Product Detail

previous pots

next pots

Let's keep in touch!

Transparent Automobile Paint Car Repair Coating Auto Body Filler Polyester Putty